Preparation and Analysis of New Hybrid PAEK Nano-Composites Containing MWCNT, Inorganic and Organic Nano-Particles

Abstract

In modern era light weight material with complex shape and high material properties is required for advanced applications at room temperature. In this concern, the experimental study analysis to observe the effect of different nanofiller material like GO, MWCNT, NH2 and COOH modified MWCNT as organic nanofiller and WS2 and MoS2 as inorganic nanofiller reinforced in pure PAEK. This experimental study focuses on incorporation of organic and inorganic nanofillers separately and combine as hybrid nanofiller nanocomposite. On preparation of PAEK nano-composite and hybrid nanocomposite the comparative study of mechanical properties like tensile, flexural and impact is carried out. The nano-composites were prepared by melt compounding method. Scanning Electron Microscopy confirm the homogenous dispersion and alignment of nanofilers. The hybrid nano-composites show highest tensile strength as compared to the organic and in-organic nanofiller nanocomposite. As the percentage of MWCNT increases from 0.2  to 1 wt% , the properties of nano-composites decreases due agglomeration tendency of MWCNT that results in low load transfer capacity of nanocomposite, therefore agglomeration tendency of MWCNT required to be controlled for preparation of nano-composite and this is achieved by reinforcing Hybrid nanofillers to pure PAEK matrix. However, organic filler shows 75 MPa to 83 MPa tensile properties and which is lower compared to in-organic and hybrid filler due agglomeration tendency of organic nanofiller confirmed by SEM analysis.